Супердуплексні нержавіючі сталізабезпечують набагато вищу міцність і стійкість до корозії, ніж 316. Таким чином, безпосередня відповідь - так - супер дуплекс краще, ніж316.
'Duplex' stainless steels are a family of stainless steels that contain a mixed microstructure of austenite and ferrite phases. They offer a combination of good corrosion resistance and high strength, making them suitable for a wide range of applications. Super duplex stainless steels have a higher content of alloying elements, such as chromium, nickel, and molybdenum, compared to duplex stainless steels. They are based upon 25% chromium content. As such, super duplex stainless steels have up to four times the tensile strength of 316 stainless steel, and considerably better corrosion resistance. An alloys resistance to pitting corrosion can be usefully summarised by the PREN value, which is the 'Pitting Resistance Equivalent number'. The PREN for super duplex stainless steels is >40, порівняно з PREN для 316 з 25.
Однак, незважаючи на дуже привабливі переваги супердуплексної нержавіючої сталі над 316, є деякі обмеження. Супердуплексна нержавіюча сталь втрачає значну частину своєї ударної в’язкості нижче -50°C, тоді як для 316 ударна в’язкість в основному зберігається до кріогенних температур. Супердуплексна нержавіюча сталь обмежена тривалою робочою температурою нижче 250°C, тоді як 316 може використовуватися до 870°C (за умови, що це низьковуглецева сталь).316Lабо стабілізовані титаном варіанти 316Ti, щоб уникнути міжкристалітної корозії).
Супер дуплексну нержавіючу сталь, звичайно, важче обробляти, враховуючи її набагато вищу міцність. Вважається, що їх складніше зварювати, але їх можна легко виготовити за допомогою відповідного обладнання та процедур.